Glan Taylor polarizer is made of two same birefringent material prisms that are assembled with an air space. Its length to aperture ratio which is less than 1.0 makes it a relatively thin polarizer. The polarizer with no side escape windows is suitable for low to medium power application where the side rejected beams are not required .The angular field of different materials of polarizers is listed below for comparison.
Features
l Air-spaced
l Close to Brewster’s Angle Cutting
l High Polarization Purity
l Short Length
l Suitable for low to medium power application where the rejected beam is not required
Glan Taylor Polarizer
Material |
α-BBO,Calcite,YVO4 |
Wavelength Rangee |
α-BBO: 190-3500nm,Calcite: 350-2300nm, YVO4:400-5000nm |
Extinction Ratio |
α-BBO: <5x10-6,Calcite: <5x10-5,YVO4: 5x10-6 |
Parallelism: |
<1 arc Min |
Surface Quality |
20/10 |
Beam Deviation |
<3 arc minutes |
Wavefront Distortion |
<λ/4@633nm |
Damage Threshold |
>200MW/cm2 |
Coating |
Single MgF2 |
Mount |
Black Anodized Aluminium |
Below are the standard porducts of Glan-Taylor Polarizer:
α-BBO Glan-Taylor-Polarizer
Part No. |
Wavelength Range(nm) |
Extinction Ratio |
Angular Field(°) |
C.A.Φa (mm) |
O.D.Φd (mm) |
L±0.1 (mm) |
AGTP206 |
200-270 |
<5x10-5 |
>6.0 |
5 |
15 |
8 |
AGTP215 |
13.5 |
30 |
15 |
|||
AGTP220 |
18 |
38 |
19 |
|||
AGTP306 |
300-700 |
<5x10-6 |
>6.0 |
6 |
15 |
15 |
AGTP315 |
15 |
30 |
23 |
|||
AGTP320 |
20 |
38 |
29 |
|||
AGTP706 |
700-3000 |
<5x10-6 |
>6.0 |
6 |
15 |
15 |
AGTP715 |
15 |
30 |
23 |
|||
AGTP720 |
20 |
38 |
29 |
Calcite Glan-Taylor Polarizer
Part No. |
Wavelength Range(nm) |
Extinction Ratio |
Angular Field((°) |
C.A.Φa (mm) |
O.D.Φd (mm) |
L±0.1 (mm) |
CGTP706 |
350-2300 |
<5x10-5 |
>7.7° |
6 |
15 |
15 |
CGTP715 |
15 |
30 |
23 |
|||
CGTP720 |
20 |
38 |
29 |
YVO4 Glan-Taylor Polarizer
Part No. |
Wavelength Range(nm) |
Extinction Ratio |
Angular Field(°) |
C.A.Φa (mm) |
O.D.Φd (mm) |
L±0.1 (mm) |
YGTP806 |
500-4000 |
<5x10-6 |
≤6.5 |
5 |
15 |
7 |
YGTP815 |
13.5 |
30 |
12 |
|||
YGTP820 |
18 |
38 |
15 |